OM10 is highly toughened structural Low Tg resin for press and autoclave curing for the needs of structural parts used in Automotive Industry. OM10 prepreg cures at both press and Autoclave with long out-life of 4 weeks at ambient temperature.
OM11, a resin structural Low Tg prepreg that specifically customized for fatigue resistance part production in Industry. OM11 prepreg materials can be curable with Autoclave and Press.
Glass fiber or carbon fiber reinforced composites offer advantages of high corrosion resistance and high strength-to-weight ratio than traditional wood or steel materials. Kordsa may provide different reinforcement materials including glass or carbon UD, 2D and multiaxial impregnated with epoxy. For the huge size part production, generally vacuum bag only prepregs (OM12) are recommended
OM13 is a structural resin system. It is translucent when cured.
OM14, a fast curing structural prepreg for press curing for the needs of structural parts used in Automotive Industry. Its short curing cycle and hot de-moldable nature are especially optimized for mass production at Automotive Industry with the addition of exceptionally long out life at room temperature. OM14 eliminates the need of Autoclave and Cold storage plus it is especially optimized for mass production. New resin system not only cures under 1-2 minutes at 150°C at press under isothermal curing conditions but also hot de-moldable and long out-life of one year at ambient temperature.
OM15 is for visual applications. It is translucent when cured without any white washes. It is Low Tg , about 110 °C
EF 10 and EF11 are highly toughened High Tg prepregs can be cured with autoclave (EF11 is also optimized for press molding) and used in extreme applications. The highest glass transition temperature reached with epoxy products (EF 12) is above 240 °C. High Tg EF12 resin system is used to produce structural prepregs. Optimized cure methods for these resin systems are Press and Autoclave molding.
| OM 10 |
Industrial composites, Automotive |
Structural Composites, Al Sandwich Panels |
High toughness , Opaque White When Cured, Tacky Version is Available |
 |
| OM 11 |
Industrial composites, Automotive |
Structural; fatigue applications |
Translucent when cured, good fatigue performance |
|
| OM 12 |
Industrial composites |
Structural |
Opaque White when cured, OOA Moldable |
|
| OM 13 |
Industrial composites, Automotive |
Structural, visual |
Translucent when cured |
|
| OM 14 |
Industrial composites, Automotive |
Structural |
Fast Cure, Room Temp Storages |
|
| OM15 |
Industrial composites, Automotive |
Visual composites, |
Translucent when cured; DICY free formulation water spot/white wash free composites |
|
| EF 10 |
Industrial composites, Automotive |
Structural |
Excellent mechanical and temperature performance |
|
| EF 11 |
Industrial Composites, Automotive, Aviation |
High Tg required applications, Secondary airplane structures, Engines, Helicopters |
High damage tolerance and good impact resistance |
|
| EF 12 |
Industrial Composites, Automotive, Aviation |
High Tg required applications, Primary/Secondary aircraft structures, Engines, Helicopters |
High damage tolerance and good impact resistance |
|